Thermostability of hydroxy sodalite in view of membrane applications

Sheida Khajavi*, Sina Sartipi, Jorge Gascon Sabate, Jacobus C. Jansen, Freek Kapteijn

*Corresponding author for this work

Research output: Contribution to journalArticlepeer-review

44 Scopus citations

Abstract

Hydroxy sodalite crystals were successfully synthesized using a direct hydrothermal synthesis method at different temperatures (90-140 °C) and different synthesis durations (3.5-24 h) with varying Si/Al ratios in the starting gel to determine optimal conditions for eventual membrane preparation from this material. The resulting crystals were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), inductively coupled plasma-optical emission spectroscopy (ICP-OES), in situ temperature programmed XRD up to 900 °C, and differential thermal and thermo-gravimetric analyses (DTA/TGA). The XRD patterns revealed the successful formation of pure hydroxy sodalite at all temperatures depending on the synthesis duration. The formed primary crystals had a mean size of 500 nm and tended to form clustered aggregates. Changing the Si/Al ratio of the starting gel did not have any effect on the framework composition. The ICP-OES measurements showed a framework Si:Al:Na ratio of 1:1:1.27 in all samples. In situ powder XRD and TG/DTA revealed that hydroxy sodalite loses its entire framework water in two steps and starts transforming to α-carnegieite at 700 °C and further to nepheline at 900 °C. The water loss was reversible in a partially dehydrated hydroxy sodalite sample, while a fully dehydrated sample showed no water sorption capability. Using a similar synthesis procedure, supported hydroxy sodalite coatings were manufactured. The comparison, in terms of thermal behaviour, between the supported and unsupported sodalite crystals reveals a higher thermal stability of the supported material.

Original languageEnglish (US)
Pages (from-to)510-517
Number of pages8
JournalMicroporous and Mesoporous Materials
Volume132
Issue number3
DOIs
StatePublished - Aug 1 2010

Keywords

  • Hydroxy sodalite
  • Powder synthesis
  • Zeolite stability

ASJC Scopus subject areas

  • Chemistry(all)
  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials

Fingerprint

Dive into the research topics of 'Thermostability of hydroxy sodalite in view of membrane applications'. Together they form a unique fingerprint.

Cite this