Thermal variation of current perpendicular-to-plane giant magnetoresistance in laminated and nonlaminated spin valves

F. Delille*, A. Manchon, N. Strelkov, B. Dieny, M. Li, Y. Liu, P. Wang, E. Favre-Nicolin

*Corresponding author for this work

Research output: Contribution to journalArticlepeer-review

16 Scopus citations

Abstract

The current perpendicular-to-plane (CPP) giant magnetoresistance (GMR) was investigated as a function of temperature in 500 nm diameter spin-valve pillars of the form PtMn 7 nm/AP2/Ru 0.8 nm/AP1/Cu 3.2 nm/F. AP2/RU/AP1 represents a synthetic ferrimagnetic pinned layer and F is either a simple Co 50Fe 50 5 nm free layer or a laminated (Co 50Fe 50 1 nm/Cu 0.3 nm)4/Co 50Fe 50 1 nm free layer. The purpose of the lamination is to increase the CPP resistance by taking advantage of the large CoFe/Cu interfacial resistance. As expected, we observed that the CPP resistance and absolute magnetoresistance (AΔR) are increased in the laminated structure. However, the CPP magnetoresistance ratio (AΔR) does not increase as much as expected if considering the increase in the relative resistance weight of the active part of the spin valve due to lamination. To understand this observation, the semiclassical theory of CPP GMR including bulk and interfacial spin relaxation effects was used to quantitatively interpret the data between 2 and 300 K. The quantitative analysis indicates that a quite significant spin-memory loss takes place at CoFe/Cu interfaces which reduces the expected GMR of the laminated multilayer. The spin-memory loss at Co 50Fe 50/Cu interfaces is found to be 52% at 4 K and 56% at 300 K, to be compared with 25% at 300 K for Cu/Co interfaces [Eid et al., J. Appl. Phys. 93, 3445 (2003) and Bozec et al., J. Appl. Phys. 87, 4334 (2000)].

Original languageEnglish (US)
Article number013912
JournalJournal of Applied Physics
Volume100
Issue number1
DOIs
StatePublished - 2006
Externally publishedYes

ASJC Scopus subject areas

  • Physics and Astronomy (miscellaneous)
  • Physics and Astronomy(all)

Fingerprint Dive into the research topics of 'Thermal variation of current perpendicular-to-plane giant magnetoresistance in laminated and nonlaminated spin valves'. Together they form a unique fingerprint.

Cite this