Synthesis, characterization, and thermal properties of ladderlike polyepoxysiloxanes

Yuhui Lin, K. P. Pramoda, Chaobin He, Wei Yu Chen, Tai-Shung Chung*

*Corresponding author for this work

Research output: Contribution to journalArticlepeer-review

12 Scopus citations

Abstract

Starting from trichlorosilanes and using 1,4-phenylenediamine as a template, we have synthesized some ladderlike poly(glycidyl-co-alkyl/aryl)siloxanes (polyepoxysiloxanes or polyepoxies for short). The structures of copolymers were confirmed through IR, 1H NMR, elemental analyses, and gel permeation chromatography. Curing behaviors of these polyepoxies in the absence and presence of a curing agent have been studied with DSC. It was shown that these epoxies could be cured without any curing agent. Copolymers having aromatic groups showed higher curing reactivity than those having alkyl groups. The experimental results also demonstrate that the curing reaction occurred solely via epoxy functionality, not via the condensation reaction of the hydroxy groups located at the end of polymer main chains. The thermal stability of the cured polymers was examined by thermogravimetric analysis. The results confirm that polyepoxies with aromatic groups had better thermal stability than those with alkyl groups. It was also found that polyepoxies cured with a diamine have a higher thermal stability than those cured in the absence of a curing agent.

Original languageEnglish (US)
Pages (from-to)2215-2222
Number of pages8
JournalJournal of Polymer Science, Part A: Polymer Chemistry
Volume39
Issue number13
DOIs
StatePublished - Jul 1 2001

Keywords

  • Curing
  • Epoxy
  • Ladderlike polyepoxysiloxane
  • Polysilsesquioxane
  • Thermal properties

ASJC Scopus subject areas

  • Polymers and Plastics
  • Organic Chemistry
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Synthesis, characterization, and thermal properties of ladderlike polyepoxysiloxanes'. Together they form a unique fingerprint.

Cite this