Continuous and c-oriented ZIF-69 membranes were successfully synthesized on porous alpha-alumina substrates by an in situ solvothermal method. The membranes were characterized by XRD, SEM and single-gas permeation tests. The BET measurements on crystals taken from the same mother liquor that was used for membrane synthesis yield a Langmuir surface area of 1138 m(2)/g. The stability of the membrane towards heat and different solvents were studied. Single-gas permeation experiments through ZIF-69 membranes were carried out by a vacuum method at room temperature using H-2, CH4, CO, CO2 and SF6, respectively. The permeances were in the order of H-2 > CO2 > CH4 > CO > SF6. The separation of CO2/CO gas mixture was investigated by gas chromatograph (GC) and the permselectivity of CO2/CO was 3.5 +/- 0.1 with CO2 permeance of 3.6 +/- 0.3 x 10(-8) mol m(-2) s(-1) Pa-1 at room temperature. (C) 2010 Elsevier B.V. All rights reserved.