Synthesis and characterization of a Sr0.95Y0.05TiO3-δ-based hydrogen electrode for reversible solid oxide cells

Yihan Ling, Luyang Chen, Lin Bin, Weili Yu, Tayirjan T. Isimjan, Ling Zhao, Xingqin Liu

Research output: Contribution to journalArticlepeer-review

5 Scopus citations

Abstract

Reversible solid oxide cells (RSOCs) can generate electricity as solid oxide fuel cells (SOFC) facing a shortage of electricity and can also store the electricity as solid oxide electrolysis cells (SOEC) at the time of excessive electricity. The composite Sr0.95Y0.05TiO3-δ-Sm0.2Ce0.8O1.9 (SYT-SDC) as the hydrogen electrode provides a promising alternative for a conventional Ni/YSZ. The possible charge compensation mechanism of SYT is described as Sr0.95Y0.05Ti0.95-2δ 4+Ti2δ+0.05 3+O3-δ. The Ti3+ is approximately 11.73% in the reduced SYT by XRD Rietveld refinement, electron paramagnetic resonance (EPR) and thermogravimetry (TG) analysis. Voltage-current curves and impedance spectra are measured as a function of applied voltages to characterize the cells. The bulk resistance (Ro) and the electrode polarization resistance (Rp) at open circuit voltages (OCV) at 750 °C are 9.06 Ω cm2 and 10.57 Ω cm2, respectively. The Ro values have a small amount of changes with small slopes both in the SOFC (-0.29 Ω cm2 V-1) and SOEC mode (0.5 Ω cm2 V-1), whereas the Rp values decrease all the time with the increasing voltages at both the SOFC (-2.59 Ω cm2 V-1) and SOEC mode (-9.65 Ω cm2 V-1), indicating that the electrical conductivity and electro-catalytic property of the SYT-based hydrogen electrode can be improved under the SOEC mode. This journal is
Original languageEnglish (US)
Pages (from-to)17000-17006
Number of pages7
JournalRSC Adv.
Volume5
Issue number22
DOIs
StatePublished - 2015