Surprising transformation of a block copolymer into a high performance polystyrene ultrafiltration membrane with a hierarchically organized pore structure

Rahul Shevate, Mahendra Kumar, Madhavan Karunakaran, Christian Canlas, Klaus-Viktor Peinemann

Research output: Contribution to journalArticlepeer-review

15 Scopus citations

Abstract

We describe the preparation of hierarchical polystyrene nanoporous membranes with a very narrow pore size distribution and an extremely high porosity. The nanoporous structure is formed as a result of unusual degradation of the poly(4-vinyl pyridine) block from self-assembled poly(styrene)-b-poly(4-vinyl pyridine) (PS-b-P4VP) membranes through the formation of an unstable pyridinium intermediate in an alkaline medium. During this process, the confined swelling and controlled degradation produced a tunable pore size. We unequivocally confirmed the successful elimination of the P4VP block from a PS-b-P4VPVP membrane using 1D/2D NMR spectroscopy and other characterization techniques. Surprisingly, the long range ordered surface porosity was preserved even after degradation of the P4VP block from the main chain of the diblock copolymer, as revealed by SEM. Aside from a drastically improved water flux (∼67% increase) compared to the PS-b-P4VP membrane, the hydraulic permeability measurements validated pH independent behaviour of the isoporous PS membrane over a wide pH range from 3 to 10. The effect of the pore size on protein transport rate and selectivity (a) was investigated for lysozyme (Lys), bovine serum albumin (BSA) and globulin-γ (IgG). A high selectivity of 42 (Lys/IgG) and 30 (BSA/IgG) was attained, making the membranes attractive for size selective separation of biomolecules from their synthetic model mixture solutions.
Original languageEnglish (US)
Pages (from-to)4337-4345
Number of pages9
JournalJournal of Materials Chemistry A
Volume6
Issue number10
DOIs
StatePublished - 2018

Fingerprint

Dive into the research topics of 'Surprising transformation of a block copolymer into a high performance polystyrene ultrafiltration membrane with a hierarchically organized pore structure'. Together they form a unique fingerprint.

Cite this