Structural and magnetic properties of Co65C35 nanocomposite films prepared by pulsed filtered vacuum arc deposition

Hao Wang*, S. P. Wong, W. Y. Cheung, N. Ke, W. F. Lau, M. F. Chiah, Xixiang Zhang

*Corresponding author for this work

Research output: Contribution to journalArticlepeer-review

33 Scopus citations

Abstract

In this paper, the Co65C35 nanocomposite film was prepared by pulsed filtered vacuum arc deposition. Subsequent thermal annealing was performed in a vacuum furnace (~ 8 × 10-4 Pa) at various temperatures. The films were characterized by X-ray photoelectron spectroscopy (XPS), transmission electron microscopy (TEM) and magnetic force microscopy (MFM). The magnetic properties were measured by a SQUID magnetometer. The as-deposited film was found to be amorphous and soft ferromagnets. No obvious magnetic domain structures can be observed in the MFM image, indicating the low anisotropy in the amorphous film. After annealing at a temperature between about 300°C and 350°C, the as-deposited amorphous films went through a meta-stable stage at which a cobalt carbide phase and hexagonal close-packed (hcp) crystalline cobalt co-existed. Upon increasing of annealing temperature to 400°C, the carbide phase decomposed into hcp crystalline cobalt nanograins and graphite-like carbon. Clear MFM images with obvious long-range magnetic structures can be obtained in the annealed films. The strengthened MFM images contrast implied the enhanced magneto-crystalline anisotropy owing to the nanocrystallization of Co grains within the films. The magnetic hardening was demonstrated by the round-shaped magnetic hysteresis loops.

Original languageEnglish (US)
Pages (from-to)147-151
Number of pages5
JournalMaterials Science and Engineering C
Volume16
Issue number1-2
DOIs
StatePublished - Oct 20 2001

Keywords

  • Magnetic properties CoC nanocomposite film
  • Microstructure
  • SQUID magnetometer
  • Transmission electron microscopy
  • X-ray photoelectron spectroscopy

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

Fingerprint

Dive into the research topics of 'Structural and magnetic properties of Co<sub>65</sub>C<sub>35</sub> nanocomposite films prepared by pulsed filtered vacuum arc deposition'. Together they form a unique fingerprint.

Cite this