Reticular synthesis of HKUST-like tbo MOFs with enhanced CH4 storage

Ioannis Spanopoulos, Constantinos Tsangarakis, Emmanuel Klontzas, Emmanuel Tylianakis, George Froudakis, Karim Adil, Youssef Belmabkhout, Mohamed Eddaoudi, Pantelis N. Trikalitis

Research output: Contribution to journalArticlepeer-review

144 Scopus citations

Abstract

Successful implementation of reticular chemistry using a judiciously designed rigid octatopic carboxylate organic linker allowed the construction of expanded HKUST-1-like tbo-MOF series with intrinsic strong CH4 adsorption sites. The Cu-analogue displayed a concomitant enhancement of the gravimetric and volumetric surface area with the highest reported CH4 uptake among the tbo family, comparable to the best performing MOFs for CH4 storage. The corresponding gravimetric (BET) and volumetric surface area of 3971 m2 g-1 and 2363 m2 cm-3 represent an increase of respectively 115 % and 47 % in comparison to the corresponding values for the prototypical HKUST-1 (tbo-MOF-1), and 42 % and 20 % higher than tbo-MOF-2. High pressure methane adsorption isotherms revealed a high total gravimetric and volumetric CH4 uptakes, reaching 372 cm3 (STP) g-1 and 221 cm3 (STP) cm-3 respectively at 85 bar and 298 K. The corresponding working capacities between 5-80 bar were found to be 294 cm3 (STP) g-1 and 175 cm3 (STP) cm-3 and are placed among the best performing MOFs for CH4 storage particularly at relatively low temperature (e.g. 326 cm3 (STP) g-1 and 194 cm3 (STP) cm-3 at 258 K). To better understand the structure-property relationship and gain insight on the mechanism accounting for the resultant enhanced CH4 storage capacity, molecular simulation study was performed and revealed the presence of very strong CH4 adsorption sites at the vicinity of the organic linker with similar adsorption energetics as the open metal sites. The present findings supports the potential of tbo-MOFs based on the supermolecular building layer (SBL) approach as an ideal platform to further enhance the CH4 storage capacity via expansion and functionalization of the quadrangular pillars.
Original languageEnglish (US)
Pages (from-to)1568-1574
Number of pages7
JournalJournal of the American Chemical Society
Volume138
Issue number5
DOIs
StatePublished - Jan 5 2016

Fingerprint Dive into the research topics of 'Reticular synthesis of HKUST-like tbo MOFs with enhanced CH4 storage'. Together they form a unique fingerprint.

Cite this