Progress in Understanding Degradation Mechanisms and Improving Stability in Organic Photovoltaics

William R. Mateker, Michael D. McGehee

Research output: Contribution to journalArticlepeer-review

210 Scopus citations

Abstract

Understanding the degradation mechanisms of organic photovoltaics is particularly important, as they tend to degrade faster than their inorganic counterparts, such as silicon and cadmium telluride. An overview is provided here of the main degradation mechanisms that researchers have identified so far that cause extrinsic degradation from oxygen and water, intrinsic degradation in the dark, and photo-induced burn-in. In addition, it provides methods for researchers to identify these mechanisms in new materials and device structures to screen them more quickly for promising long-term performance. These general strategies will likely be helpful in other photovoltaic technologies that suffer from insufficient stability, such as perovskite solar cells. Finally, the most promising lifetime results are highlighted and recommendations to improve long-term performance are made. To prevent degradation from oxygen and water for sufficiently long time periods, OPVs will likely need to be encapsulated by barrier materials with lower permeation rates of oxygen and water than typical flexible substrate materials. To improve stability at operating temperatures, materials will likely require glass transition temperatures above 100 °C. Methods to prevent photo-induced burn-in are least understood, but recent research indicates that using pure materials with dense and ordered film morphologies can reduce the burn-in effect.
Original languageEnglish (US)
Pages (from-to)1603940
JournalAdvanced Materials
Volume29
Issue number10
DOIs
StatePublished - Dec 22 2016
Externally publishedYes

Fingerprint

Dive into the research topics of 'Progress in Understanding Degradation Mechanisms and Improving Stability in Organic Photovoltaics'. Together they form a unique fingerprint.

Cite this