Porosity-induced relaxation of strains in GaN layers studied by means of micro-indentation and optical spectroscopy

Adel Najar, Michel Gerland, Mustapha Jouiad

Research output: Contribution to journalArticlepeer-review

20 Scopus citations

Abstract

We report the fabrication of porous GaNnanostructures using UV-assisted electroless etching of bulk GaN layer grown on c-plane sapphire substrate in a solution consisting of HF:CH3OH:H2O2. The morphology of the porous GaNnanostructures was characterized for different etching intervals using high resolution scanning electron microscopy. The geometry and size of resultant pores do not appear to be affected by the etching time; however, the pore density was augmented for longer etching time. Micro-indentation tests were carried out to quantify the indentation modulus for different porous GaNnanostructures. Our results reveal a relationship between the elastic properties and the porosity kinetics, i.e., a decrease of the elastic modulus was observed with increasing porosity. The photoluminescence(PL) and Raman measurements carried out at room temperature for the etched samples having a high degree of porosity revealed a strong enhancement in intensity. Also, the peak of the PL wavelength was shifted towards a lower energy. The high intensity of PL was correlated to an increase of scattered photons within the porous media and to the reduction of the dislocation density.
Original languageEnglish (US)
Pages (from-to)093513
JournalJournal of Applied Physics
Volume111
Issue number9
DOIs
StatePublished - May 4 2012

ASJC Scopus subject areas

  • Physics and Astronomy(all)

Fingerprint Dive into the research topics of 'Porosity-induced relaxation of strains in GaN layers studied by means of micro-indentation and optical spectroscopy'. Together they form a unique fingerprint.