Evolution of Pt Clusters on Graphene Induced by Electron Irradiation

Cezhou Dong, Wenpeng Zhu, Siyuan Zhao, Peng Wang, Hongtao Wang, Wei Yang

Research output: Contribution to journalArticlepeer-review

7 Scopus citations

Abstract

In situ low-voltage transmission electron microscopy (TEM) was performed to study the evolution of small Pt clusters on suspended graphene. Pt clusters, trapped by the edge of holes, generally take a stable shape of truncated octahedron for sizes ranging from sub-1 to ∼5 nm. The interaction to the graphene dots takes in charge when they form composite nanostructures embedded in graphene. The Pt clusters are slowly flattened due to hole enlargement under electron irradiation. The planar structure is maintained by the peripheral Pt-C bonds and instantly collapses into a three-dimensional (3D) cluster if one side is detached from the edge. Based on the heat transfer model, the thermal effect can be excluded under the experimental condition. Atomistic evolution can be attributed to the electron irradiation. Molecular dynamics simulations revealed that the evolution kinetics was found to be dominated by the surface diffusion (characterized by the migration barrier Em), the temperature (the thermal activation energy ∼5kBT), and the scattering from electrons (the maximum transferred energy Emax). The corresponding energies are comparable for the Pt cluster system, leading to similar evolution behaviors. A different scenario in graphene systems is due to the large difference in agitations, i.e., Emax ≫ Em ∼ 5kBT at 3000 K. This unique behavior comes from TEM observation, implying that electron beam irradiation can be utilized as a unique tool in shaping carbon nanostructures.
Original languageEnglish (US)
JournalJOURNAL OF APPLIED MECHANICS-TRANSACTIONS OF THE ASME
Volume80
Issue number4
DOIs
StatePublished - 2013
Externally publishedYes

Fingerprint

Dive into the research topics of 'Evolution of Pt Clusters on Graphene Induced by Electron Irradiation'. Together they form a unique fingerprint.

Cite this