Development and Characterization of P-doped Ba-122 Superconducting Tapes

D. Contarino, C. Löhnert, D. Johrendt, Alessandro Genovese, C. Bernini, A. Malagoli, M. Putti

Research output: Contribution to journalArticlepeer-review

1 Scopus citations

Abstract

Among the recently discovered Fe-based superconducting compounds, the Ba-122 phase has proved to be the more attracting for the development of powder in tube (PIT) processed conductors. In fact, after some years of development, critical current densities ($J_{c}$) of about $10^{5} A/cm^{2}$ at 4.2 K and magnetic fields up to 10 T have been obtained in$(Ba_{0.6} K_{0.4}) Fe_{2} As_{2}$, PIT wires and tapes. To develop a safe upscaling method, the synthesis of the powders is a crucial point. In order to avoid the use of highly reactive K we have developed $BaFe_{2}(P_{1-x}As_{x})_{2}$ PIT tapes. This compound has proved to be very stable and in form of crystals and thin films exhibits excellent critical current: We succeeded in manufacturing PIT tapes with this phase with $J_{c}$ values of about $10^{3}A/cm^{2}$ at 4.2K in self-field. Detailed microstructural and chemical investigations of the samples have been performed by high-resolution TEM, scanning TEM, and electron energy loss spectrometry analysis. A deformation network inside the grains that can induce strong pinning has been observed. However, chemical inhomogeneities at the grain boundaries are also present, which limit the transport current.
Original languageEnglish (US)
Pages (from-to)1-4
Number of pages4
JournalIEEE Transactions on Applied Superconductivity
Volume27
Issue number4
DOIs
StatePublished - Nov 29 2016

Fingerprint Dive into the research topics of 'Development and Characterization of P-doped Ba-122 Superconducting Tapes'. Together they form a unique fingerprint.

Cite this