Detemplation of DDR type zeolites by ozonication

Jelan Kuhn*, Jorge Gascon Sabate, Joachim Gross, Freek Kapteijn

*Corresponding author for this work

Research output: Contribution to journalArticlepeer-review

28 Scopus citations

Abstract

Ozonication is a technique which can be used to remove the template from zeolites at much lower temperatures than conventional calcination. The template removal by ozonication has been investigated for small pore zeolites of the DDR topology. The pore size of the DDR type zeolites (4.4 × 3.6 Å) is smaller than the molecular diameter of ozone (4.6 Å). The detemplation of these zeolites confirms the assumption of ozone breaking down into radicals at the zeolite surface before diffusing through the pore system. All-silica DDR (DD3R), all-silica ZSM-58 and aluminum containing NaZSM-58 (Si/Al = 170) have been synthesized. The crystal size distributions of the materials show the DD3R crystals have an average size of 2.7 μm, while the ZSM-58 sample consists of 6.1 μm hexagonal shaped crystals. The NaZSM-58 material consists of globular aggregates of 36 μm, consisting of small 1 μm primary particles. The ozonication was carried out at 473 K using 100 ml min-1 of a mixture of 80 g Nm-3 ozone in oxygen. DD3R was completely detemplated in 38 h of ozonication, showing porosity characteristics equal to that of a thermally calcined sample. The all-silica ZSM-58 and NaZSM-58 samples were detemplated for 75% in 38 h and 90% in 8 h, respectively, as compared to the thermally calcined samples. The incomplete detemplation is expected to be due to the larger size of the SDA for ZSM-58 (MTI) compared to the SDA for DD3R (1-ADA). The lower template removal of the all-silica ZSM-58 is attributed to the larger crystal size.

Original languageEnglish (US)
Pages (from-to)12-18
Number of pages7
JournalMicroporous and Mesoporous Materials
Volume120
Issue number1-2
DOIs
StatePublished - Apr 1 2009

Keywords

  • DD3R
  • DDR
  • Detemplation
  • Ozone
  • ZSM-58
  • Zeolite

ASJC Scopus subject areas

  • Chemistry(all)
  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials

Fingerprint

Dive into the research topics of 'Detemplation of DDR type zeolites by ozonication'. Together they form a unique fingerprint.

Cite this