Colloidal CdSe/Cu3P/CdSe nanocrystal heterostructures and their evolution upon thermal annealing

Luca De Trizio, Francesco De Donato, Alberto Casu, Alessandro Genovese, Andrea Falqui*, Mauro Povia, Liberato Manna

*Corresponding author for this work

Research output: Contribution to journalArticlepeer-review

29 Scopus citations

Abstract

We report the synthesis of colloidal CdSe/Cu3P/CdSe nanocrystal heterostructures grown from hexagonal Cu3P platelets as templates. One type of heterostructure was a sort of "coral", formed by vertical pillars of CdSe grown preferentially on both basal facets of a Cu3P platelet and at its edges. Another type of heterostructure had a "sandwich" type of architecture, formed by two thick, epitaxial CdSe layers encasing the original Cu3P platelet. When the sandwiches were annealed under vacuum up to 450 °C, sublimation of P and Cd species with concomitant interdiffusion of Cu and Se species was observed by in situ HR- and EFTEM analyses. These processes transformed the starting sandwiches into Cu 2Se nanoplatelets. Under the same conditions, both the pristine (uncoated) Cu3P platelets and a control sample made of isolated CdSe nanocrystals were stable. Therefore, the thermal instability of the sandwiches under vacuum might be explained by the diffusion of Cu species from Cu 3P cores into CdSe domains, which triggered sublimation of Cd, as well as out-diffusion of P species and their partial sublimation, together with the overall transformation of the sandwiches into Cu2Se nanocrystals. A similar fate was followed by the coral-like structures. These CdSe/Cu 3P/CdSe nanocrystals are therefore an example of a nanostructure that is thermally unstable, despite its separate components showing to be stable under the same conditions.

Original languageEnglish (US)
Pages (from-to)3997-4005
Number of pages9
JournalACS Nano
Volume7
Issue number5
DOIs
StatePublished - May 28 2013

Keywords

  • annealing
  • cation exchange
  • doping
  • heterostructures
  • nanocrystals

ASJC Scopus subject areas

  • Engineering(all)
  • Materials Science(all)
  • Physics and Astronomy(all)

Fingerprint Dive into the research topics of 'Colloidal CdSe/Cu3P/CdSe nanocrystal heterostructures and their evolution upon thermal annealing'. Together they form a unique fingerprint.

Cite this