Amorphous/crystalline silicon interface defects induced by hydrogen plasma treatments

Jonas Geissbühler*, Stefaan De Wolf, Bénédicte Demaurex, Johannes P. Seif, Duncan T.L. Alexander, Loris Barraud, Christophe Ballif

*Corresponding author for this work

Research output: Contribution to journalArticlepeer-review

66 Scopus citations

Abstract

Excellent amorphous/crystalline silicon interface passivation is of extreme importance for high-efficiency silicon heterojunction solar cells. This can be obtained by inserting hydrogen-plasma treatments during deposition of the amorphous silicon passivation layers. Prolonged hydrogen-plasmas lead to film etching. We report on the defect creation induced by such treatments: A severe drop in interface-passivation quality is observed when films are etched to a thickness of less than 8 nm. Detailed characterization shows that this decay is due to persistent defects created at the crystalline silicon surface. Pristine interfaces are preserved when the post-etching film thickness exceeds 8 nm, yielding high quality interface passivation.

Original languageEnglish (US)
Article number231604
JournalApplied Physics Letters
Volume102
Issue number23
DOIs
StatePublished - Jun 10 2013

ASJC Scopus subject areas

  • Physics and Astronomy (miscellaneous)

Fingerprint Dive into the research topics of 'Amorphous/crystalline silicon interface defects induced by hydrogen plasma treatments'. Together they form a unique fingerprint.

Cite this